Instruction and Application: Stainless steel submerged arc welding wire and flux, low metal impurity elements C, S, P, etc. Mechanical properties and corrosion resistance good.The welding process has good performance, easy to remove slag and low alloy.Suitable for welding of austenitic stainless steel 304L (022Cr19Ni10) type.
Typical Chemical Composition of the wire (%)
C |
Si |
Mn |
S |
P |
Cr |
Ni |
δFe |
0.015 |
0.11 |
1.73 |
0.008 |
0.019 |
20.31 |
9.85 |
9 |
Typical Chemical Composition of the all-weld metal (%)
Si |
Mn |
S |
P |
Cr |
Ni |
δFe |
|
0.022 |
0.23 |
1.51 |
0.009 |
0.021 |
19.93 |
9.73 |
8.5 |
Mechanical properties of all-weld metal
Temperature |
Tensile strength Rm(MPa) |
Yield strength Rp(MPa) |
Elongation A(%) |
Bending Test (GB/T 2653) |
Room temperature |
570 |
425 |
40 |
No Cracks |
Physical and chemical analysis of the flux (%)
|
Mechanical inclusion |
S |
P |
SJ601A |
0.14 |
0.018 |
0.020 |
All-welded metal radio-graphic testing:
According to NB / T 47103.2, The radio-graphic testing should not be less than class AB and the quality grade of all-welded metal should not be less than Class I at least.
Reference range (DC﹢)
Sizeφ(mm) |
Amperage (A) |
Volt (V) |
Speed (mm/min) |
φ3.2 |
400-450 |
28-32 |
520-580 |
Φ4.0 |
450-500 |
28-32 |
520-580 |
Notice:
1.Redry the flux at 300℃-350℃ for 1hours.
2.The welding consumables surface rust, oil and other impurities to be clean.
3.The welding slag must be cleaned up in the multi-pass welding. The interpass temperature should be controlled below 150℃.