Instruction and Application: Low hydrogen type 0Cr13Ni4Mo stainless steel welding rod, stable of arc, small splash, metal deposition of chemical stability, wear resistance and crack resistance good. DC reverse. Used for welding of the same type stainless steel, also can be used for corrosion resistant, wear-resisting surfacing welding.
Typical Chemical Composition of the all-weld metal (％)
|
C |
Si |
Mn |
S |
P |
Cr |
Ni |
Mo |
|
0.046 |
0.27 |
1.41 |
0.005 |
0.018 |
13.52 |
3.78 |
0.52 |
Mechanical properties of all-weld metal
|
Temperature |
Tensile strength Rm(MPa) |
Elongation A(%) |
|
Room temperature |
870 |
16 |
All-welded metal radio graphic testing:
According to NB/T 47013.2, the radio graphic testing should not be less than class AB and the quality grade of all-welded metal should not be less than Class I at least.
Reference Current(DC+):
|
Electrodes Sizeφ（mm) |
Φ2.5 |
Φ3.2 |
Φ4.0 |
Φ5.0 |
|
Amperage (A) |
60-90 |
90-120 |
120-160 |
170-210 |
Notice:
1.The electrode with titanium-calcium coating must be stoved at 200-300℃ for 1 hours prior to use.
2.The welding consumables surface rust, oil fouling and other impurities must be cleaned up.
3.The welding slag must be cleaned up in the multi-pass welding. The inter-pass temperature should be controlled below 150 ℃.
Contact us