Instruction and Application: Titanium acid - type drug skin 309S (06Cr23Ni13) ultra-low carbon stainless steel, with good welding process performance, good slag removal, small splash, anti-stomatal performance and anti-crack performance. Alternating current and dc. Used in petrochemical, pressure vessel, inner wall surfacing, carbon steel and stainless steel heteroplasmic material welding, or for 304L (022Cr19Ni10) ultra-low carbon stainless steel corrosion resistant surfacing.
Typical Chemical Composition of the all-weld metal (％)
|
C |
Si |
Mn |
S |
P |
Cr |
Ni |
|
0.021 |
0.72 |
1.50 |
0.004 |
0.018 |
23.13 |
13.00 |
Mechanical properties of all-weld metal
|
Temperature |
Tensile strength Rm(MPa) |
Elongation A(%) |
Bending Test (GB/T 2653) |
|
Room temperature |
570 |
37 |
No Cracks |
All-welded metal radio graphic testing:
According to NB/T 47013.2, the radio graphic testing should not be less than class AB and the quality grade of all-welded metal should not be less than Class I at least.
Reference Current(DC+):
|
Electrodes Sizeφ（mm) |
Φ2.5 |
Φ3.2 |
Φ4.0 |
Φ5.0 |
|
Amperage (A) |
60-90 |
90-120 |
120-160 |
170-210 |
Notice:
1.The electrode with titanium-calcium coating must be stoved at 200-300℃ for 1 hours prior to use.
2.The welding consumables surface rust, oil fouling and other impurities must be cleaned up.
3.The welding slag must be cleaned up in the multi-pass welding. The inter-pass temperature should be controlled below 150 ℃.