Instruction and Application: Low hydrogen drug skin 347H (06Cr18Ni11Nb) stainless steel, with good welding process performance, corrosion resistance and crack resistance. Good stomatal resistance, DC reverse, all-position welding. Used for welding of low carbon resistant titanium or niobium stabilized stainless steel.
Typical Chemical Composition of the all-weld metal (%)
C |
Si |
Mn |
S |
P |
Cr |
Ni |
Nb |
0.054 |
0.76 |
1.45 |
0.004 |
0.018 |
20.12 |
10.21 |
0.69 |
Mechanical properties of all-weld metal
Temperature |
Tensile strength Rm(MPa) |
Elongation A(%) |
Bending Test (GB/T 2653) |
Room temperature |
575 |
38 |
No Cracks |
All-welded metal radio graphic testing:
According to NB/T 47013.2, the radio graphic testing should not be less than class AB and the quality grade of all-welded metal should not be less than Class I at least.
Reference Current(DC+):
Electrodes Sizeφ(mm) |
Φ2.5 |
Φ3.2 |
Φ4.0 |
Φ5.0 |
Amperage (A) |
60-90 |
90-120 |
120-160 |
170-210 |
Notice:
1.The electrode with titanium-calcium coating must be stoved at 200-300℃ for 1 hours prior to use.
2.The welding consumables surface rust, oil fouling and other impurities must be cleaned up.
3.The welding slag must be cleaned up in the multi-pass welding. The inter-pass temperature should be controlled below 150 ℃.