Instruction and Application: The 304L (022Cr19Ni10) type ultra-low carbon stainless steel with titanium-calcium coating is used in the welding of petrochemical industry, power station boilers, food machinery, medical equipment, fertilizer and other associated equipment in other industries. The electrode with titanium-calcium coating has good welding processing properties, stable arc, little spatter. The electrode can be operated in all welding positions and with AC-DC dual-use.
Typical Chemical Composition of the all-weld metal (%)
C |
Si |
Mn |
S |
P |
Cr |
Ni |
0.029 |
0.73 |
1.37 |
0.007 |
0.018 |
19.87 |
10.33 |
Mechanical properties of all-weld metal
Temperature |
Tensile strength Rm(MPa) |
Elongation A(%) |
Bending Test (GB/T 2653) |
Room temperature |
585 |
44 |
No Cracks |
All-welded metal radio graphic testing:
According to NB/T 47013.2, the radio graphic testing should not be less than class AB and the quality grade of all-welded metal should not be less than Class I at least.
Reference Current(DC+):
Electrodes Sizeφ(mm) |
Φ2.5 |
Φ3.2 |
Φ4.0 |
Φ5.0 |
Amperage (A) |
60-90 |
90-120 |
120-160 |
170-210 |
Notice:
1.The electrode with titanium-calcium coating must be stoved at 200-300℃ for 1 hours prior to use.
2.The welding consumables surface rust, oil fouling and other impurities must be cleaned up.
3.The welding slag must be cleaned up in the multi-pass welding. The inter-pass temperature should be controlled below 150 ℃.