Instruction and Application: H09MnSHG is a special-purpose wire and flux for submerged arc welding of pipeline steel SJ111G combinations, SJ111G ultra low hydrogen sintered flux, basicity B>2.5, flux process performance, deposited metal purity and low content of S,P, good mechanical properties. Applies to X65, X70, X80 pipeline steel and welding of low alloy high strength steel structures of steel, especially meet the needs high corrosion resistance and low temperature impact -30℃.

Typical Chemical Composition of the wire(％)

Typical Chemical Composition of the all-weld metal(％)

Mechanical properties of All-weld metal 

*In practice, the heat treatment system shall be formulated separately by the supply and demand parties or by the conditions of the working conditions (such as the thickness of the specimen).

SSC Test: (NACE TM 0177，GB/T 4157/2006 )

No crack over 0.1mm in the sample through thickness direction. Threshold stress σ th ≥ 247MPa

HIC Test:（NACE TM 0284）

H_D (Mercury method): ≤ 4.0ml/100g

Physical and chemical analysis of the flux(％)

All-weld metal radio-graphic testing:

According to NB / T 47013.2, the radio-graphic detecting technique should not be less than class AB and the quality grade of all-weld metal should not be less than Class I.

Reference range (DC﹢)

Notice：

1.Redry the flux at 300-350℃ for 2 hours.

2.Cleaning the oil stain, rust and moisture of the weldment surface before welding.

3.Multi-pass welding must clean the welding slag. Each layer is controlled below 150℃.